今天给大家分享的是2015年4月份 《Catalysis Communications》上发表的一篇名为:Enhanced activity of MnxW0.05Ti0.95 ? xO2 ? δ for selective catalytic reduction of NOx with ammonia by self-propagating high-temperature synthesis
文章摘要如下:
A series of TiO2 supported MnWOx catalysts MnxW0.05Ti0.95 ? xO2 ? δ (x = 0.05, 0.1, 0.15) were synthesized by solution combustion method. The Mn0.10W0.05Ti0.85O2 ? δ catalyst showed highest activity in NH3-SCR reaction within a broad temperature range of 200 °C–400 °C. XRD and TEM results indicate that the active Mn and W species are highly dispersed over TiO2 support in the form of nanoparticles (4–7 nm). The TEM and H2-TPR results also suggest that a MnWOx phase has been formed on the TiO2, which is beneficial for the activity of the MnxW0.05Ti0.95 ? xO2 ? δ catalysts in the high temperature range of 280 °C–400 °C.
该文章中材料表征采用的是美国麦克仪器3Flex
详情可参考下面链接:
http://www.sciencedirect.com/science/article/pii/S1566736715000369
更多
Micromeritics 加入马尔文帕纳科成为颗粒表征领域的全球领导者
厂商
2024.07.19
探索电池性能的微观世界:麦克仪器电池材料孔隙率表征新方案
厂商
2024.07.09
Micromeritics 麦克仪器硬碳/硅碳孔隙表征解决方案
厂商
2024.05.13
CIBF重庆,Micromeritics带来锂电新角度
厂商
2024.04.24