今天给大家分享的是2014年5月份 《International Journal of Hydrogen Energy》上发表的一篇名为:Promotional effect of Ru on the activity and stability of Co/SBA-15 catalysts in dry reforming of methane
文章摘要如下:
The catalysts in this study were prepared via the “two-solvents” impregnation method and labeled as: xCo and yRu-xCo/SBA-15 (x = 12 wt%, y = 0.75–1.125–1.5 wt%). These catalysts were characterized by N2 sorption, X-Ray Diffraction (XRD) techniques, Transmission Electron Microscopy (TEM) analyses and Temperature Programmed Oxidation/Reduction (TPO/TPR). The catalytic activity of mono (Co) and bimetallic (Co–Ru) supported on SBA-15 was investigated in the dry reforming of methane (DRM) reaction.
TEM and XRD data showed that Ruthenium species were mainly located outside the porosity of the support, while cobalt species were present inside and outside the pores. The addition of ruthenium promoted the reducibility of cobalt catalysts to lower temperatures and a complete reduction of the Ru–Co/SBA-15 catalysts at T < 500 °C was observed. The promotional effect was also shown in the dry reforming reaction where hydrogen started to form on the 0.75Ru–12Co/SBA-15, 1.125Ru–12Co/SBA-15 and 1.5Ru–12Co/SBA-15 at 600, 500 and 510 °C respectively. Nevertheless, the 12Co/SBA-15 displayed low activity for methane dry reforming reaction. Deactivation via coke deposition affects all the catalysts. The TPO of the 1.125Ru–12Co/SBA-15 catalyst shows an oxidation of carbaneous species at T = 250 °C.
该文章中材料表征采用的是美国麦克仪器AutoChem 2920
详情可参考下面链接:
http://www.sciencedirect.com/science/article/pii/S0360319914006946
更多
Micromeritics 加入马尔文帕纳科成为颗粒表征领域的全球领导者
厂商
2024.07.19
探索电池性能的微观世界:麦克仪器电池材料孔隙率表征新方案
厂商
2024.07.09
Micromeritics 麦克仪器硬碳/硅碳孔隙表征解决方案
厂商
2024.05.13
CIBF重庆,Micromeritics带来锂电新角度
厂商
2024.04.24