对于相分离的研究有多种方法，流变学的特点在于可以实时的检测到由于微观结构变化导致的粘弹性的变化。在紫外固化的过程中，结构的变化更短促，只有通过哈克流变仪才能快速的分辨出相分离。

对于涂料等复杂流体的流变表征，通常只集中在流动行为的某一些部分，难于表现整个的行为特征。通过哈克旋转流变仪，可以对涂料的屈服应力、触变形、流平性、垂挂性等性能得到完整的评估，从而为配方研究和质量控制提供有用的信息。

The recently introduced HAAKE MARS platform features a modular design that allows researchers to adapt the system quickly and easily for different applications and test needs. All rheological measurements can be performed in CR (controlled rate), CS (controlled stress) and CD (controlled deformation) modes, in rotation and in oscillation. A new normal force sensor allows negative normal forces to be measured for tensile test applications. The new oven is designed for ease of handling, functionality and a wide range of measurements. The oven chamber can be observed through viewing windows. The independent movement of the chamber halves promotes fast sample trimming and cleaning. The oven uses a combination of radiant and convective heating, which provides fast temperature ramps and extremely small temperature gradients. When not in use, it can quickly be parked out of the measuring area. The HAAKE MARS sytem is easy to operate, and the base frame offers room for expansion with simple adjustments to accommodate additional modules and to customize applications. All relevant components, including the measuring head and electronics, can be interchanged. The rugged frame is made from precision casting designed to increase its strength and to expand its capabilities for future measurement components. The HAAKE RheoWin 3 software and new sensor recognition tool allow measurement and evaluation functions to be performed and saved easily. In addition, an optional polymer software package allows the user to calculate master curves, spectra and molecular weight distributions. For more information about the MARS platform and Thermo Electron Corporation’s

用振荡流变仪，我们首先进行低频率和形变测量。在线性粘弹区测量粘度。此区测量，结构不是不可逆形变。因此我们测量到完整结构的粘度。然后我们测量高剪切下的粘度。样品的结构将被完全破坏。最后我们重复第一步条件重测量。我们观察结构随时间的恢复。

用频率扫描，可以分析材料不同的应用，类似于粘度测量。一般应用研究从低频（静止行为）到高频如挤出、喷涂等。基本上，高弹性模量样品行为类似固体，不流动，稳定性好。高粘性模量样品行为似液体，易流动，稳定性差。

在进行各种振荡测试以调查许多样品之前，定义线性粘弹区很重要。近一步的测试（如频率扫描的频率）很有必要在样品的可逆状态进行。在线性粘弹区，所施加的压力和形变是可逆的。这可以用橡胶带的拉伸形象比较。如果您给橡胶带施加的力不太大，力撤消后它将恢复到原来状态。但如果您施加力太大，橡胶带将产生不可恢复形变直至断裂。

蠕变和恢复显示一定应力下粘性和弹性的时间响应不同。通过蠕变和恢复测量，我们了解有关样品的流平、垂驰、沉淀以及分子量等信息。

屈服值是使样品刚刚开始流动所需要的力。我们可以认为有屈服值的液体在静止时行为类似固体。 通过测量屈服值，我们可以了解样品的稳定性、使用和加工性能。

粘度曲线通常基于理论模型。用今天的新技术，我们可以看剪切过程的样品结构变化以对大分子结构的变化有更好的理解。为了了解正在发生什么，我们用HAAKE可视流变仪Rheoscope来测量。

触变性是指结构的破坏与恢复。通过触变性影响，我们观察结构被第一次破坏后的重新建立。通过测量触变性，我们可以了解有关样品的流平性、实际使用情况和加工情况。

流动曲线是表示粘度随剪切速率的变化，我们定义一些典型的现象： 1粘度同剪切速率无关（牛顿流体） 2粘度随剪切速率增加而下降（假塑性流体） 3粘度随剪切速率增加而增加（胀塑性流体） 通过测量不同剪切速率下粘度我们将了解物质的行为。 通过测量不同剪切速率下粘度我们可以预测不同条件下样品的行为。我们可以考虑样品的行为、外观、口感和加工性。