Surface energy of metal containing amorphous carbon films deposited by
2006-01-13 09:27
浏览:2132次
分享:
资料摘要:
Metal containing amorphous carbon (a-C:Me) films including a-C:Al, a-C:Ti, a-C:Ni, a-C:Si were prepared by the filtered
cathodic vacuum arc (FCVA) technique with metal-carbon (5 at.% metal) composite targets. The substrate bias ranging from floating to 1000 Vwas applied. The wettability of the films was examined using the VCA Optima system from AST Products, Inc. Three types of liquid with different polarities were used to study the surface energy changes of the films. X-ray photoelectron spectroscopy (XPS) was used to analyze the composition and chemical state of the films. Atomic force microscopy (AFM) was employed to characterize the morphology and roughness of the films. The contact angle of the a-C:Me films remains relatively constant with different substrate bias. The Al containing films show the highest contact angle with water, which reaches as high
as 1018. The Si containing films show the lowest contact angle approximately 648. The contact angles of Ni and Ti containing
films are approximately 808, 978, respectively. The harmonic-mean method was used to calculate the polar and depressive component of the surface energy. The absorption of oxygen on the surface plays an important role on the polar component of the a-C:Me films. The formation of Al–O and Ti–O bonds is responsible for their lower polar component. The metal state Ni results in higher polar component. However, the Si–O bond is contributed to the high polar component of a-C:Si films. As all films are atomic scale smooth, the RMS roughness is below 0.5 nm, the roughness does not have obvious effect on the surface energy.
下载本篇资料:
Surface energy of metal containing amorphous carbon films deposited by
773KB
推荐资料
Thermofisher Labserv CO150 CO2培养箱,易于操作和维护,为您细胞培养提供了良好的生存环境,并且添加了有效的湿热灭菌功能,是您细胞安心培养的“兵工厂”。
熟悉ALPHA 1-2 LDplus冻干机的使用者都了解,其广泛应用于植物提取物、生物样品、药物制剂研究中的冻干实验。但除了这些典型的应用,仍有一些其他典型实验,也是可以用到ALPHA 1-2 LDplus的。那我们就来看看,还有哪些是我们未知或不熟悉的典型应用:
德国Christ公司是专业生产真空离心浓缩仪的厂家,有着60多年的历史。就其浓缩仪中样品温度的变化,我们进行了详细的数据记录(图1、图2所示),从图1我们发现,当真空值设为7mbar,腔体加热温度设为79℃时,离心腔在61~79℃逐渐升温,对应的转子温度是51.1~71.7℃逐渐升温,而样品温度在14.7~18.2度之间。
离心机是实验室最常用的仪器设备,在任何实验中,离心时的容量需求以及转速表现是使用者最关心的两个方面,那我们就来梳理下常规实验中所需的离心容量及转速情况: