负性光刻胶NR9-8000

NR9-8000
Negative Resist NR9-8000 is a negative tone photoresist designed for thick film applications and is
compatible with UV exposure tools emitting at the 365 nm exposure wavelength, including wafer
steppers, scanning projection aligners, proximity printers and contact printers.
These are the advantages of NR9-8000 over other resists: -superior resolution capability -high
photospeed which translates into high exposure throughput -fast develop time -superior temperature
resistance of up to 100℃ -superior selectivity in RIE process -easy resist removal in Resist
Remover RR4 -shelf life exceeding 3 years at room temperature storage.
The formulation and processing of NR9-8000 were designed with regard to occupational and
environmental safety. The principal solvent in NR9-8000 is cyclohexanone and development of
NR9-8000 is accomplished in a basic water solution.
Properties
♦ Solids content: 39%-43%
♦ Principal solvent: cyclohexanone
♦ Appearance: light yellow liquid
♦ Coating characteristic: very uniform, striation free
♦ Film thickness:
Coating Spin
Speed (rpm)
Spin Time
(s)
1
st
Soft Hotplate
Bake Time
(s) 70℃
2
nd
Soft Hotplate
Bake Time
(s) 150℃
Post Exposure
Hotplate Bake
Time (s) 100℃
Film Thickness
(nm)
210 30 360 followed by 180 120 95000-105000
320 30 360 followed by 120 60 55000-65000
750 40 180 followed by 120 60 30000-35000
1000 40 0 120 60 16500-17500
2000 40 0 120 60 9000-10000
3000 40 0 120 60 8000-8300
4000 40 0 120 60 6500-6800
♦ Sensitivity at 365 nm exposure wavelength for 1 μm thick film: 21 mJ/cm²
♦ Guaranteed shelf life at 25℃ storage: 3 years
Processing
1 Application of resist by spin coating at a selected spin speed for a time designated in a film
thickness vs. spin speed table above.
2 Start dispensing Edge Bead Remover EBR2 simultaneously on top and bottom surface of
spinning coated substrate through nozzles 0.5-1.0 cm from an edge of a substrate as soon as
edge bead forms (3-5 s after ceasing resist dispense).
3 Softbake procedure is determined by film thickness. Please refer to bake instructions on
page 1.
4 Resist exposure in a tool emitting light at 365 nm wavelength. Please determine 365 nm
exposure light intensity (mW/cm²) with a proper gage. Multiply resist thickness (μm) by 21
mJ/cm² to obtain exposure dose. Divide expose dose (mJ/cm²) by light intensity (mW/cm²) at
365 nm wavelength to obtain exposure time (s).
5 100℃ hotplate bake for a time depending on a film thickness. Please refer to bake
instructions on page 1.
6 Resist development in Resist Developer RD6 by spray or immersion at 20-25 ℃.
Development time for an 8 μm thick film is 40 s and for 100 μm thick film is 330 s.
7 Resist rinse in deionized water until water resistivity reaches prescribed limit.
8 Drying of resist.
9 Removal of resist in Resist Remover RR4 or in acetone.
The above procedure refers to substrates, which are good conductors of heat such as silicon, GaAs,
InP, etc. Bake times need to be increased 3.5 times for substrates, which are poor conductors of heat
such as glass.
Handling Precautions
Negative Resist NR9-8000 is a flammable liquid. Handle it with care. Keep it away from heat,
sparks and flames. Use adequate ventilation. It may be harmful if swallowed or touched. Avoid
contact with liquid, vapor or spray mist. Wear chemical goggles, rubber gloves and protective
coating.