中国客户在国际刊物上发表的文章：Fabrication and characterization of hydrophobic PVDF hollow fiber membranes for desalination through direct contact membrane distillation

The mixture of inorganic salt LiCl and soluble polymer polyethylene glycol (PEG) 1500 as non-solvent additive was introduced to fabricate hydrophobic hollow fiber membrane of polyvinylidene fluoride (PVDF) by phase inversion process, using N,N-dimethylacetamide (DMAc) as solvent and tap water as the coagulation medium. Compared with other three membranes from PVDF/DMAc, PVDF/DMAc/LiCl and PVDF/DMAc/PEG 1500 dope solution, it can be observed obviously by scanning electron microscope (SEM) that the membrane spun from PVDF/DMAc/LiCl/PEG 1500 dope had longer finger-like cavities, ultra-thin skins, narrow pore size distribution and porous network sponge-like structure owing to the synergistic effect of LiCl and PEG 1500. Besides, the membrane also exhibited high porosity and good hydrophobicity. During the desalination process of 3.5 wt% sodium chloride solution through direct contact membrane distillation (DCMD), the permeate flux achieved 40.5 kg/m2 h and the rejection of NaCl maintained 99.99% with the feed solution at 81.8 ◦C and the cold distillate water at 20.0 ◦C, this performance is comparable or even higher than most of the previous reports. Furthermore, a 200 h continuously desalination experiment showed that the membrane had stable permeate flux and solute rejection, indicating that the as-spun PVDF hollowfiber membrane may be of great potential to be utilized in the DCMD process.