Layertec金属反射镜 Metallic Mirrors
Layertec金属反射镜 Metallic Mirrorsa Unprotected Gold Mirror Layertec无保护膜镀金反射镜Coating 140770Au unprotectedHR (0°, 800-20 000 nm) 98 %HR s (45°, 800-20 000 nm) 98 %HR p (45°, 800-20 000 nm) 97 %激光损伤阈值LIDT6/ 0.5 J/cm 2 795 nm 42 fs 1 kHz ? 80 μm WRCP Budapest基材尺寸No.ImperfectionsItem #? 12.7 mm | t 6.35 mmA45 / 2 x 0.025142064? 25.0 mm | t 6.35 mmB45 / 2 x 0.04142065? 50.0 mm | t 9.5 mmC35 / 6 x 0.0414206625 × 25 mm | t 6.35 mmD25 / 2 x 0.0414206725 × 36 mm | t 6.35 mmE25 / 3 x 0.0414207050 × 50 mm | t 9.5 mmF35 / 6 x 0.04142073b Protected Gold Mirror Layertec保护膜镀金反射镜Coating 140777Au + protection layerHR (0°, 800-4 000 nm) 95 %HR s (45°, 800-4 000 nm) 95 %HR p (45°, 800-4 000 nm) 94 %激光损伤阈值LIDT6/ 0.2 J/cm 2 795 nm 42 fs 1 kHz ? 80 μm WRCP Budapest基材尺寸No.ImperfectionsItem #? 12.7 mm | t 6.35 mmA45 / 2 x 0.025142074? 25.0 mm | t 6.35 mmB45 / 2 x 0.04142075? 50.0 mm | t 9.5 mmC35 / 6 x 0.0414207625 × 25 mm | t 6.35 mmD25 / 2 x 0.0414207725 × 36 mm | t 6.35 mmE25 / 3 x 0.0414207850 × 50 mm | t 9.5 mmF35 / 6 x 0.04142079C Protected Silver Mirror, 600-1000 nm Layertec保护膜镀银反射镜Coating 140780Ag + protection layer, fs-opt. 600-1000 nmHR (0°, 600-1 000 nm) 97 %HR s (45°, 600-1 000 nm) 96 %HR p (45°, 600-1 000 nm) 96 %| GDD-R s,p (0-45°, 600-1 000 nm) | 激光损伤阈值LIDT6/ 5 J/cm 2 1 064 nm 7 ns 10 Hz ? 480 μm LAYERTEC6/ 0.7 J/cm 2 795 nm 42 fs 1 kHz ? 80 μm WRCP Budapestd Protected Silver Mirror, 800-2000 nm Layertec保护膜镀银反射镜Coating 140831Ag + protection layer, fs-opt. 800-2 000 nmHR (0°, 800-2 000 nm) 97 %HR s (45°, 800-2 000 nm) 98 %HR p (45°, 800-2 000 nm) 97 %| GDD-R s,p (0-45°, 800-2 000 nm) | 激光损伤阈值LIDT6/ 5 J/cm 2 1 064 nm 7 ns 10 Hz ? 480 μm LAYERTEC6/ 0.7 J/cm 2 795 nm 42 fs 1 kHz ? 80 μm WRCP Budapest基材尺寸No.ImperfectionsItem #? 12.7 mm | t 6.35 mmA45 / 2 x 0.025142093? 25.0 mm | t 6.35 mmB45 / 2 x 0.04142094? 50.0 mm | t 9.5 mmC35 / 6 x 0.0414209625 × 25 mm | t 6.35 mmD25 / 2 x 0.0414209925 × 36 mm | t 6.35 mmE25 / 3 x 0.0414210150 × 50 mm | t 9.5 mmF35 / 6 x 0.04142100e Protected Aluminum Mirror, UV-range Layertec保护膜镀银反射镜Coating 142407Al enhanced, 260-360 nm opt.HR s,p (0-45°, 260-360 nm) ≥ 90 %| GDD-R s,p (0-45°, 260-360 nm) | 基材尺寸No.ImperfectionsItem #? 12.7 mm | t 6.35 mmA45 / 2 x 0.025142415? 25.0 mm | t 6.35 mmB45 / 2 x 0.04142416? 50.0 mm | t 9.5 mmC35 / 6 x 0.0414241725 × 25 mm | t 6.35 mmD25 / 2 x 0.0414241825 × 36 mm | t 6.35 mmE25 / 3 x 0.0414241950 × 50 mm | t 9.5 mmF35 / 6 x 0.04142420f Protected Aluminum Mirror, 266 + 400 + 800 nm Layertec保护膜镀银反射镜Coating 140842Al + protection layerHR s,p (0-45°, 266 + 400 + 800 nm) 80 %| GDD-R s,p (0-45°, 266 + 400 + 800 nm) | for polarization-sensitive and low-power ultrafast applications基材尺寸No.ImperfectionsItem #? 12.7 mm | t 6.35 mmA45 / 2 x 0.025142069? 25.0 mm | t 6.35 mmB45 / 2 x 0.04142071? 50.0 mm | t 9.5 mmC35 / 6 x 0.0414209125 × 25 mm | t 6.35 mmD25 / 2 x 0.0414209225 × 36 mm | t 6.35 mmE25 / 3 x 0.0414209550 × 50 mm | t 9.5 mmF35 / 6 x 0.04142097德国Layertec公司创建于 1990年. 凭借多年在光学镜片的设计开发和生产经验,已成为全球知名的光学镜片厂商,LAYERTEC的镜片品质非常出众,广泛赢得客户的赞誉。光学镜片应用波长范围从157-2940nm,包括了科研以及工业上主流的激光器的应用,材质有YAG, Sapphire,CaF2,IR-fused silica,Fused Silica,BK7,尺寸大部份为0.5inch-2inch。Layertec专注于提供激光光学元件的镀膜,波长范围从 VUV(157nm及以下) 到 NIR波段(~4um)。最常见的光学镀膜类型是高反射镜(从正入射或者AOI=45°的转向镜),用于输出耦合的部分反射镜,以及分束器和用于窗口和透镜的抗反射膜。对于更复杂的激光器镀膜,包括3个以上波长的高反射率(例如激光器波长和倍频波长),以及3个以上波长的高透射率(例如泵浦波长,倍频或者抑制其他激光波长)。宽带反射镜,针对平滑群延迟和群延迟色散光谱优化的反射镜,这些在宽带激光输出应用中会用到,例如染料激光器,钛宝石激光器,光参量震荡器(OPO)和飞秒激光器。除了反射率和透射率,激光应用的镀膜必须满足低光学损耗和高激光损伤阈值。在VIS和NIR波段的溅射光学镀膜具有低杂散光和低吸收损耗(数量级都在10–5)。磁控溅射镀膜的HR镜反射率或者部分反射镜的反射透射率之和都超过99.9%。最近测量了在溅射和蒸发镀膜中的NIR波长吸收损耗都在3-30ppm。在VIS-NIR波长范围,蒸发镀膜会产生杂散光损失大约10-3级,在UV和VUV波长可以达到10-2。尽管如此,蒸发镀膜在UV波长的吸收损耗比较低。在CW和纳秒激光器光学元件的损伤主要跟热效应有关,例如增大的吸收,镀膜材料的固有吸收或者缺陷造成的吸收, 或者 镀膜较差的热导率 以及较低的熔化温度。 高能量的镀膜要求控制镀膜材料的固有特性以及减少膜层的缺陷。皮秒和飞秒激光元件的激光损伤主要是场强效应造成的。针对这类激光器的高功率镀膜要求非常特殊的设计。根据ISO 11254-1 (cw- 激光损伤阈值LIDT and 1 on 1–激光损伤阈值LIDT, 例如单脉冲 激光损伤阈值LIDT), ISO 11254-2 (S on 1, 例如多脉冲 激光损伤阈值LIDT) 以及 ISO 11254-3 (一定数量的脉冲激光损伤阈值LIDT )标准中对激光损伤阈值激光损伤阈值LIDT的定义要求激光系统工作在单频模式下,精确的光束诊断和在线/离线损伤探测系统。因为这个原因,数量有限的配有少数几种激光器的测量系统可以使用(例如Laserzentrum Hannover 公司的1064nm)。对于比较特殊的激光器波长例如氩离子激光器(488nm或者514nm),没有测量系统可以用来验证激光损伤阈值LIDT数据。