晶体温控炉

优质进口LuAG:Ce晶体或Ce:LuAG晶体或铝酸镥石榴石为闪烁体，可根据用户要求做成薄片的荧光屏，典型的直径范围为2mm到50mm,厚度范围为0.1mm到5mm.当然我们也可以提供其他各种形状和大小的探测器，包括：棱镜型/球形或薄片型，并提供当面抛光，双面抛光和多面抛光。并提供铝、鋯或氧化铟锡的窗口等多种选择。LuAG:Ce, Lutetium Aluminum Garnet activated by cerium (chemical formula Lu3Al5O12), is a relatively dense and fast scintillation material. Its density of 6.73 g/cm3 is about 94% of the density of BGO (7.13 g/cm3). Its decay time is much faster (70 ns) than that of BGO (300 ns). This is of advantage in time dependent and coincidence measurements. The wavelength of scintillation emission is about 535 nm, which is ideal for photodiode and avalanche diode readout. The material can also be used for imaging screens, similarly to YAG:Ce. A particular advantage of LuAG:Ce is its higher density resulting in thinner screens with higher spatial resolution. The material is mechanically and chemically stable, and can be machined into a variety of shapes and sizes including prisms, spheres and very thin plates.LuAG:Ce晶体或Ce:LuAG晶体或铝酸镥石榴石可用于电子、X射线、伽玛射线、UV和EUV的探测，具有如下典型应用：荧光屏或成像屏 我们提供的闪烁屏或成像屏是由YAG:Ce, LuAG:Ce和YAP:Ce晶体材料构成。目前提供如下三种选择： *标准的成像屏：直径可达50mm,厚度0.5-0.1mm.用于：X射线、电子、UV和EUV的成像。 *带衬底超薄屏：超薄LuAG:Ce晶体或Ce:LuAG晶体或铝酸镥石榴石厚度可小到为0.005mm，耦合到光纤光学、玻璃、石英等衬底上使用。可用的规格是：厚度为0.010mm直径最大为40mm, 厚度为0.005mm直径最大为25mm. *独立薄成像屏: 这种超薄LuAG:Ce晶体或Ce:LuAG晶体成像屏是独立使用的闪烁屏，不需要耦合到衬底上。目前可用的规格如下： LuAG:Ce晶体或Ce:LuAG晶体或铝酸镥石榴石成像屏：厚度0.050mm的屏直径最大是50mm,厚度为0.025mm的闪烁屏的最大资金是10mm LuAG:Ce晶体或Ce:LuAG晶体或铝酸镥石榴石成像屏：厚度0.1mm的屏直径最大是50mm, 厚度为0.050mm的屏的最大直径是10mm. 这种独立使用的闪烁屏非常脆，极易损坏，为此，我们为您提供了一种刚玉外壳用于保护成像屏，或者可提供陶瓷或钢铁外壳保护。 导光元件 我们为各种探测器提供不同的导光元件，根据不同的闪烁材料和应用，我们提供如下多种材料的导光元件： 有机玻璃（PMMA),近紫外的特殊有机玻璃，光学玻璃BK7, 石英玻璃，有机玻璃或石英玻璃光纤，蓝宝石，YAG 电镜探测器 我们提供独具特色的电镜探测器采用YAG:Ce,YAP:Ce,CRY18材料制成，特别适合电子探测和成像，并配备多样的导光元件，非常方便测量。 闪烁探测器：提供多种类型的探测器用于电镜，这些探测器具有工作寿命长，荧光效率好等特点，提供的标准产品有： 标准探测器：SE, BSE,TEM,Dark Field (ADF) 特殊探测器：带镜头的探测器，阵列探测器，阴极荧光探测器（CL)

优质进口LuAG:Ce晶体或Ce:LuAG晶体为闪烁体，可根据用户要求做成薄片的荧光屏，典型的直径范围为2mm到50mm,厚度范围为0.1mm到5mm.当然我们也可以提供其他各种形状和大小的探测器，包括：棱镜型/球形或薄片型，并提供当面抛光，双面抛光和多面抛光。并提供铝、鋯或氧化铟锡的窗口等多种选择。LuAG:Ce, Lutetium Aluminum Garnet activated by cerium (chemical formula Lu3Al5O12), is a relatively dense and fast scintillation material. Its density of 6.73 g/cm3 is about 94% of the density of BGO (7.13 g/cm3). Its decay time is much faster (70 ns) than that of BGO (300 ns). This is of advantage in time dependent and coincidence measurements. The wavelength of scintillation emission is about 535 nm, which is ideal for photodiode and avalanche diode readout. The material can also be used for imaging screens, similarly to YAG:Ce. A particular advantage of LuAG:Ce is its higher density resulting in thinner screens with higher spatial resolution. The material is mechanically and chemically stable, and can be machined into a variety of shapes and sizes including prisms, spheres and very thin plates.LuAG:Ce晶体或Ce:LuAG晶体可用于电子、X射线、伽玛射线、UV和EUV的探测，具有如下典型应用：荧光屏或成像屏 我们提供的闪烁屏或成像屏是由YAG:Ce, LuAG:Ce和YAP:Ce晶体材料构成。目前提供如下三种选择： *标准的成像屏：直径可达50mm,厚度0.5-0.1mm.用于：X射线、电子、UV和EUV的成像。 *带衬底超薄屏：超薄LuAG:Ce晶体或Ce:LuAG晶体厚度可小到为0.005mm，耦合到光纤光学、玻璃、石英等衬底上使用。可用的规格是：厚度为0.010mm直径最大为40mm, 厚度为0.005mm直径最大为25mm. *独立薄成像屏: 这种超薄LuAG:Ce晶体或Ce:LuAG晶体成像屏是独立使用的闪烁屏，不需要耦合到衬底上。目前可用的规格如下： LuAG:Ce晶体或Ce:LuAG晶体成像屏：厚度0.050mm的屏直径最大是50mm,厚度为0.025mm的闪烁屏的最大资金是10mm LuAG:Ce晶体或Ce:LuAG晶体成像屏：厚度0.1mm的屏直径最大是50mm, 厚度为0.050mm的屏的最大直径是10mm. 这种独立使用的闪烁屏非常脆，极易损坏，为此，我们为您提供了一种刚玉外壳用于保护成像屏，或者可提供陶瓷或钢铁外壳保护。 导光元件 我们为各种探测器提供不同的导光元件，根据不同的闪烁材料和应用，我们提供如下多种材料的导光元件： 有机玻璃（PMMA),近紫外的特殊有机玻璃，光学玻璃BK7, 石英玻璃，有机玻璃或石英玻璃光纤，蓝宝石，YAG 电镜探测器 我们提供独具特色的电镜探测器采用YAG:Ce,YAP:Ce,CRY18材料制成，特别适合电子探测和成像，并配备多样的导光元件，非常方便测量。 闪烁探测器：提供多种类型的探测器用于电镜，这些探测器具有工作寿命长，荧光效率好等特点，提供的标准产品有： 标准探测器：SE, BSE,TEM,Dark Field (ADF) 特殊探测器：带镜头的探测器，阵列探测器，阴极荧光探测器（CL)

Yb:LuAG是应用前景广阔的激光工作物质,Yb:LuAG更适合激光二极管泵浦系统，并不适合传统的掺钕激光系统的泵浦结构。Yb:LuAG晶体或掺镱钇铝石榴石可输出0.94 μm激光，与传统的Nd:YAG晶体相比，Yb:LuAG晶体或掺镱钇铝石榴石具有更大的吸收带宽,更长的上能级寿命，3-4倍更低的单位泵浦功率热负荷。Yb:LuAG晶体或掺镱钇铝石榴石在高功率半导体泵浦激光器领域，被人们认为是取代Nd:YAG 晶体的最佳选择。更多Yb:LuAG晶体资料请浏览：领先的进口精密激光光学器件旗舰型服务商--孚光精仪！Yb:LuAGUndoped YAG has higher thermal conductivity compared to undoped LuAG. Increasing Yb3+ doping leads to a drop of in thermal conductivity. In Yb:YAG thermal conductivity decreases to almost half of its initial value, while Yb:LuAG displays a drop of only 10%. Heavily doped Yb:LuAG can be advantageously used in thin disc lasers.Physical properties Yb:YAG Yb:LuAG Pump wavelength941 nm938 nmAbsorption cross section8,2 . 10-21 cm27,2 . 10-21 cm2Emission wavelength1030 nm1031 nmEmission cross section2,1 . 10-20 cm22,6 . 10-20 cm2Laser transition2F5/2 -- 2F7/22F5/2 -- 2F7/2Refractive transition1,821,84Crystal structurecubiccubic