CdSe晶体 硒化镉晶体 中远红外波片
产品介绍: CdSe晶体非常适用于制作红外光学元件,偏振片,1/4、1/2波片,分束镜,基底,真空沉积靶材,DFM频率转换器。产品参数:结构 Wurtzite (Hexagonal)密度: 5.81 g/ cm3杨氏模量:5×1011 dyne/cm2热膨胀系数 (500 K):α 1=6.26×10-6/K α 3=4.28×10-6/K比热:0.49 J/gK 热导率 (at 25 °C):0.04 W/cmK最大透过率 (λ =2.5-15 μm):≥ 71 %吸收系数. (λ =10.6 μm):≤ 0.0015 cm-1 (including 2 surfaces)折射率 (λ =10.6 μm):2.4258 (no), 2.4437 (ne)电阻率a). low: 1 Ohm*cm b). high: about 10^11 Ohm*cm最大单晶尺寸:?40mm X L: 80 mm最大红外光学元件尺寸:?50mm X L:10 mm OR plate 50 mm X 15 mm X 12 mm硒化镉产品透过率曲线:直径/宽度1-50 mm厚度/长度0.1-150 mm晶向(0001), (10-10), (11-20)表面质量As-cut, 80/50, 60/40 per MIL-0-13830CdSe 棒, 晶圆 和基片CdSe 晶体尺寸纯度99.995%, 99.999%颗粒尺寸0.01- 10 mm应用举例CdSe晶体应用于12.3um波片时,单片晶体的厚度:λ/2波片@12.3um:Order: 1 Half-wave plate thickness: 0.3575 [mm]Order: 2 Half-wave plate thickness: 0.7151 [mm]Order: 3 Half-wave plate thickness: 1.0726 [mm]Order: 4 Half-wave plate thickness: 1.4302 [mm]Order: 5 Half-wave plate thickness: 1.7877 [mm]Order: 6 Half-wave plate thickness: 2.1453 [mm]Order: 7 Half-wave plate thickness: 2.5029 [mm] Order: 8 Half-wave plate thickness: 2.8604 [mm]Order: 9 Half-wave plate thickness: 3.2180 [mm]Order: 10 Half-wave plate thickness: 3.5755 [mm]λ/2波片波片@12.3um:Order: 1 Quarter-wave plate thickness: 0.1787 [mm]Order: 2 Quarter-wave plate thickness: 0.3575 [mm]Order: 3 Quarter-wave plate thickness: 0.5363 [mm]Order: 4 Quarter-wave plate thickness: 0.7151 [mm]Order: 5 Quarter-wave plate thickness: 0.8938 [mm]Order: 6 Quarter-wave plate thickness: 1.0726 [mm]Order: 7 Quarter-wave plate thickness: 1.2514 [mm]Order: 8 Quarter-wave plate thickness: 1.4302 [mm]Order: 9 Quarter-wave plate thickness: 1.6090 [mm]Order: 10 Quarter-wave plate thickness: 1.7877 [mm] 更多晶体相关产品 碲化锌晶体 ZnTe晶体 铌酸锂晶体 LiNbO3晶体 硒化锌晶体 ZnSe晶体 硒化镓晶体 GaSe晶体 硫化锌晶体 ZnS晶体 磷化镓晶体 GaP晶体 有机晶体 DAST晶体 有机晶体 DSTMS晶体 有机晶体 OH1晶体