ASTM系美国材料与试验协会的英文缩写,其英文全称为American Society for Testing and Materials。该技术协会成立于1898年。
炭黑物理性能测试ASTM D412 ,D3182,D3192 ,D3191用工业参比炭黑IRB (industry reference black),新标样IRB 9替代IRB8.
标准参比炭黑 standard reference carbon black 一种具有典型物化性能、质量均匀、性能稳定的橡胶用炭黑。主要作为炭黑生产厂和橡胶制品厂验证试验重现性及再现性的标准物质。目前炭黑工业和橡胶工业常用的标准参比炭黑是ASTM SRB (standard reference black),前后推出9个系列的SRB, 新系列为SRB 8,IRB (industry reference black)是用于炭黑橡胶性能的工业参比炭黑,已推出IRB 1---9#,目前新推出的是IRB9。
IRB 9与IRB8 相比,有多项不同,请见下表
ASTM 测试方法 | 测试项目 | 测试结果 |
D3191, Method B | Carbon Black in SBR, Tensile Strength, Difference from IRB#7 | -0.33 MPa (-48 psi) |
D3191, Method B | Carbon Black in SBR, Tensile Stress at 300% Elongation, Difference from IRB#7 | -0.63 MPa (-91 psi) |
D3191, Method B | Carbon Black in SBR, Ultimate Elongation, Difference from IRB#7 | 5.5 % |
D3191, Method C | Carbon Black in SBR, Tensile Strength, Difference from IRB#7 | -0.16 MPa (-23 psi) |
D3191, Method C | Carbon Black in SBR, Tensile Stress at 300% Elongation, Difference from IRB#7 | -0.54 MPa (-78 psi) |
D3191, Method C | Carbon Black in SBR, Ultimate Elongation, Difference from IRB#7 | 9.4 % |
D3192, Method B | Carbon Black in NR, Tensile Strength, Difference from IRB#7 | -0.03 MPa (-4 psi) |
D3192, Method B | Carbon Black in NR, Tensile Stress at 300% Elongation, Difference from IRB#7 | -0.09 MPa (-13 psi) |
D3192, Method B | Carbon Black in NR, Ultimate Elongation, Difference from IRB#7 | 4.2 % |
D3192, Method C | Carbon Black in NR, Tensile Strength, Difference from IRB#7 | -0.21 MPa (-30 psi) |
D3192, Method C | Carbon Black in NR, Tensile Stress at 300% Elongation, Difference from IRB#7 | -0.36 MPa (-52 psi) |
D3192, Method C | Carbon Black in NR, Ultimate Elongation, Difference from IRB#7 | -0.2 % |
保修期: 1年
是否可延长保修期: 是
现场技术咨询: 有
免费培训: 免费安装上门培训
免费仪器保养: 收费服务
保内维修承诺: 免费维修
报修承诺: 72小时内到达现场维修
B&E其它行业专用工业标准参比炭黑的工作原理介绍
其它行业专用工业标准参比炭黑的使用方法?
B&E工业标准参比炭黑多少钱一台?
其它行业专用工业标准参比炭黑可以检测什么?
其它行业专用工业标准参比炭黑使用的注意事项?
B&E工业标准参比炭黑的说明书有吗?
B&E其它行业专用工业标准参比炭黑的操作规程有吗?
B&E其它行业专用工业标准参比炭黑报价含票含运吗?
B&E工业标准参比炭黑有现货吗?
最多添加5台