仪器简介:
1) 中/英文软件
2) 加装DayLight滤镜可用于光伏材料光老化试验, 更换AM1.5滤镜后可用于光伏电池预衰减试验.
BR-UL-Xenon Ultraviolet Light Exposure Chamber
Implementation of standards:
① UL 1703-2008 Polymeric materials (quote UL 746C-2006“Ultraviolet Light Exposure”, spectral distribution conform to ASTM G155-2005)
② VDE 0126-5:2008 Junction box “Weather resistance test”, VDE 0126-3:2009 Connector “Weather resistance”,spectral distribution conform to ISO 4892-2-2006
③ ETAG 002-2000, ASTM C1184-2000 Silicone sealant UV age test, spectral distribution conform to ASTM G155-2005
④ General specification of crystalline silicon solar cell for terrestrial application: Cell maximum power in early light attenuation ratio test
![]() Effective area of irradiation: 500×400mm Measurement point or range: 300~400nm, 290~800nm, 340nm/nm, 420nm/nm Irradiation uniformity: better than ±10% at 312×312mm Irradiation deviation: ±2W/m2@300~400nm Temperature control range: RT~90°C±2.5°C Air temperature control range: 20~80°C With refrigeration compressor, spray system Irradiation, temperature and spray: Program control Irradiation and temperature closed loop control… | ![]() |
Measurement point or range: 300~400nm, 290~800nm, 340nm/nm, 420nm/nm
Irradiation uniformity: better than ±10% at 312×312mm
Irradiation deviation: ±2W/m2@300~400nm
Temperature control range: RT~90°C±2.5°C
Air temperature control range: 20~80°C
With refrigeration compressor, spray system
Irradiation, temperature and spray: Program control
Irradiation and temperature closed loop control...
① DayLight filter: for junction box and connector test, spectral distribution conform to ASTM G155 and ISO 4892-2 requirements.
② AM1.5 filter (option): for cell maximum power in early light attenuation ratio test, spectral distribution conform to IEC 60904.9 Class C requirements.
Spectral after filter comparison ASTM G155:
Wavelengh range | Transmission after filter | Benchmark solar | ASTM G155 | Radiation precent after filter |
(<290nm) | 0.01% | 0~0.15% | 0~0.15% | 0.02% |
(290~320nm) | 2.85% | 5.80% | 2.6~7.9% | 4.34% |
(320~360nm) | 23.90% | 40.00% | 28.3~40.0% | 36.46% |
(360~400nm) | 38.79% | 54.20% | 54.2~67.5% | 59.18% |
Total UV | 65.54% | 100.00% | 100.00% | 100.00% |
UL 1703 (UL 746C) test results discriminant:
Physical-property consideration | Material test method |
Functional support | Tensile strength or Flexural strength (The ultraviolet-exposed side is to be in contact with the two loading points when using the three-point loading method.) |
Impact resistance | Tensile impact, Izod impact, or Charpy impact |
用户单位 | 采购时间 |
---|---|
JA Solar Holdings Co.,Ltd. (Hefei) | 2011-09-01 |
Shanghai Electrical Apparatus Research Institute | 2011-06-01 |
Jiangsu Yunyi Electric Co.,Ltd. | 2011-03-01 |
Shandong JinJing Energy-saving Glass Co.,Ltd. | 2010-06-01 |
JiangSu JiuDing Solar Energy System Co.,Ltd. | 2010-06-01 |
Chinese Academy of Sciences Key Laboratory - New Thin-film Solar Cell | 2008-06-01 |
最多添加5台