Mg和Ni机械合金化过程中的显微组织演变-加州大学(美国)
2015-03-11 09:54
浏览:128次
分享:
资料摘要:
This study investigates the microstructural evolution during mechanical alloying of Mg and Ni, and during subsequent heat treatments
of SPEX milled powders. The milling was performed under an inert argon atmosphere, employing two different ball-to-powder ratios (BPR):
10:1 and 20:1. It was observed that a large number of defects were produced during the ?rst hours of milling. These defects led to the amorphi-
zation of part of the system, and promoted an extensive re?nement of the microstructure as well. Later on, the formation of the Mg2Ni
compound due to the crystallization of the amorphous phase was observed. The microstructural details showed us that a possible
complete sequence of phase transformations during milling of pure Mg and Ni could be: Mgc +Nic →Mgnc +Nic →amorphous +
Ninc +Mgnc →amorphous +Ninc +Mg2Ninc →Mg2Ninc, where c and nc stand for crystalline and nanocrystalline, respectively. On the other
hand, subsequent heat treatments of the milled powder showed that the amorphous phase could also be transformed into Mg2Ni by heating.
Finally, the knowledge of the evolution of the microstructure during milling and annealing were combined to propose an optimal processing
route to ef?ciently obtain the Mg2Ni compound.
下载本篇资料:
g和i机械合金化过程中的显微组织演变加州大学美国.pdf
776KB
相关资料
锂离子电池(LIBs)是便携式电子设备和电动工具的能量存储设备,并具有作为替代燃料车辆能源的巨大潜力。SPEX Mixer/Mill是一种高能球磨机,最近在关键研究中用于消除制造过程中对环境有影响的物质。要了解更多关于这项研究的信息,请访问链接https://bit.ly/2Tqe7kH
液相色谱-串联质谱法分析水、固体、生物固体和组织样品中的全氟烷基和多氟烷基物质(PFAS)——美国环境保护署水办公室
当需要纯化手性化合物时,ACCQPrep HP150可以配备手性柱,可以很容易地进行这种类型的纯化。由于反式二苯乙烯氧化物是手性纯化的标准物,因此它被用作其他手性化合物的模型。
蒸气压和密度是原油、汽油及其中间体最重要的质量参数之一。根据GB/T 11059,ASTM D6377(原油蒸气压),SH/T 0794,ASTM D5191(汽油蒸气压) 和SH/T 0604,ASTM D4052(密度)的测试标准,可在炼油厂的质检室以及整个分配链,如在终端、存储设施,甚至直接在使用移动实验室进行测试。