简介:【中文摘要】 以明胶为分散剂采用溶胶-凝胶法制备了纳米晶TiO2粉末.通过XRD、TG-DTA、AFM、N2吸附-解吸等手段,考察了明胶对TiO2煅烧过程中相变和平均粒径的影响;用光催化降解甲基橙检测了明胶用量对样品光催化活性的影响.结果表明:明胶的存在简介:【中文摘要】 以明胶为分散剂采用溶胶-凝胶法制备了纳米晶TiO2粉末.通过XRD、TG-DTA、AFM、N2吸附-解吸等手段,考察了明胶对TiO2煅烧过程中相变和平均粒径的影响;用光催化降解甲基橙检测了明胶用量对样品光催化活性的影响.结果表明:明胶的存在抑制了TiO2由无定形向锐钛矿的相变,降低了锐钛矿向金红石的相变温度;同时,TiO2纳米晶的平均粒径也随明胶用量的增加而减小.600℃煅烧样品的光催化活性随明胶用量的增加而提高;800℃煅烧样品在mG∶mTBOT(明胶与钛酸四丁酯的质量比)=1∶8时,具有最高的光催化活性.
【英文摘要】 Nanocrystalline TiO_2 powders were prepared with gelatin dispersants by sol-gel method.The effects of gelatin on phase transformation and average particle sizes of nanocrystalline TiO_2 during calcination were investigated by the means of XRD,TG-DTA,AFM,and N_2 adsorption-desorption.Moreover,the effects of gelatin dosage on photocatalytic activity of samples were evaluated from an analysis of the photodegradation of methyl orange.The experimental results indicate that the gelatin has effects of inhibiting p...详细>