简介:【中文摘要】 采用均相沉淀法,在低温(90℃)、低pH值(8-9)、短时间(3-3.5 h)条件下成功地合成了系列Ba1-xSrxTiO3(BST) 和BaZrxTi1-xO3(BZT)固溶体.通过XRD、化学分析法、SEM和AFM等手段表征了固溶体的结构、组成和形貌.结果表明:BST,BZT的晶胞常数简介:【中文摘要】 采用均相沉淀法,在低温(90℃)、低pH值(8-9)、短时间(3-3.5 h)条件下成功地合成了系列Ba1-xSrxTiO3(BST) 和BaZrxTi1-xO3(BZT)固溶体.通过XRD、化学分析法、SEM和AFM等手段表征了固溶体的结构、组成和形貌.结果表明:BST,BZT的晶胞常数随组成呈线性关系,符合Vegard定律,该系列固溶体为完全互溶固溶体,且目标产物组成精确,颗粒为球形,分布均匀.初步讨论了复合矿化剂的均相化作用及羟基释放作用、分散剂对BST,BZT晶粒的聚集生长及分散机理.
【英文摘要】 A series of Ba1-xSrxTiO3(BST) and BaZrxTi1-xO3(BZT) solid solutions have been synthesized through the homogeneous phase precipitation route at low temperature (90℃) under low pH (8-9) in a short time (3-3.5 h). Structure, composition and morphology of those solid solutions were studied respectively by XRD, chemical analysis, SEM and AFM methods. The results showed that the cell parameters of them were linearly related with the composition of them, which was in accord with Vegard''s law, and the powders of th... 详细>