类金刚石 (DLC) 镀膜锗窗口片

有效孔径 (%):

90

涂层规格:

AR: Ravg ≤0.5% @ 8000 - 12000nm

边缘:

Fine Ground

努氏硬度 (kg/mm2) :

780

平行度（弧分）:

<1

基底:

Germanium (Ge)

表面质量:

60-40

波长范围 (nm):

8000 - 12000

Coating Abrasion:

AR: Moderate, per MIL-C-48497A Paragraph 4.5.3.3

DLC: Severe, per MIL-C-675C Paragraph 4.5.10

Coating Adhesion:

AR: per MIL-C-48497A Paragraph 4.5.3.1

DLC: per MIL-M-13508C Paragraph 4.4.6

Coating Humidity:

AR: per MIL-C-48497A Paragraph 4.5.3.2

DLC: ≥24 Hours per MIL-C-675C paragraph 4.5.8

Coating Salt Solubility:

AR: N/A

DLC: ≥24 Hours Immersion per MIL-C-675C paragraph 4.5.7

Coating Salt Spray:

AR: N/A

≥24 Hours per MIL-C-675C paragraph 4.5.9

Coating Solubility and Cleaning:

AR: per MIL-C-48497A Paragraph 4.5.4.2

DLC: N/A

Coating Temperature (°F):

AR: -80 to +160 per MIL-C-48497A Paragraph 4.5.4.1

DLC: -80 to +160 per MIL-M-13508C Paragraph 4.4.4

Coating Wiper Durability:

AR: N/A

DLC: ≥5,000 Wipes of Sand/Slurry per TS-1888

注意 :

Arrow on substrate edge points towards DLC coated surface

25.00 +0.0/-0.1

1.00 ±0.1

S1: DLC Coating   S2: BBAR (8000-12000nm)

13-795

25.00 +0.0/-0.1

3.00 ±0.1

S1: DLC Coating   S2: BBAR (8000-12000nm)

13-796

50.00 +0.0/-0.1

1.00 ±0.1

S1: DLC Coating   S2: BBAR (8000-12000nm)

13-797

50.00 +0.0/-0.1

3.00 ±0.1

S1: DLC Coating   S2: BBAR (8000-12000nm)

13-798

75.00 +0.0/-0.1

5.00 ±0.1

S1: DLC Coating   S2: BBAR (8000-12000nm)

13-799

100.00 +0.0/-0.1

6.00 ±0.1

S1: DLC Coating S2: BBAR (8000-12000nm)

21-087