回复m3122601发表于:2020/9/5 8:53:49悬赏金额:
6积分 状态:
未解决
[img=,690,517]https://ng1.17img.cn/bbsfiles/images/2018/12/201812050830468451_7424_3122601_3.jpg!w690x517.jpg[/img][img=,690,517]https://ng1.17img.cn/bbsfiles/images/2018/12/201812050831125273_4748_3122601_3.jpg!w690x517.jpg[/img][img=,690,517]https://ng1.17img.cn/bbsfiles/images/2018/12/201812050831212653_7205_3122601_3.jpg!w690x517.jpg[/img][img=,690,517]https://ng1.17img.cn/bbsfiles/images/2018/12/201812050831281751_4929_3122601_3.jpg!w690x517.jpg[/img][img=,690,517]https://ng1.17img.cn/bbsfiles/images/2018/12/201812050831379073_6910_3122601_3.jpg!w690x517.jpg[/img][img=,690,517]https://ng1.17img.cn/bbsfiles/images/2018/12/201812050831449781_5681_3122601_3.jpg!w690x517.jpg[/img][img=,690,517]https://ng1.17img.cn/bbsfiles/images/2018/12/201812050831556943_9251_3122601_3.jpg!w690x517.jpg[/img][img=,601,435]https://ng1.17img.cn/bbsfiles/images/2018/12/201812050841286801_7407_3122601_3.png!w601x435.jpg[/img]
25#钢,正火处理后出现大面积的带有针状铁素体的组织,在同一根试棒下做了拉力试验光谱金相,对比了一下机械性能成分和热处理,同炉同成分试棒的金相同样是有大量的针状铁素体,但是成分及机械性能都没有问题,如果正常正火处理哪怕温度或是保温时间不够的话也是出现晶粒度大一些也没有出现过这种情况 ,这种组织形态是否算是铸态组织?请大家帮忙分析一下造成的原因,是铸件本身的原因,还是热处理参数设置还是有问题 ,如何能解决掉这个情况,还有倒数第二张照片出现的情况更是一次也没有发现过,边缘位置为很好的正火状态,但是中间位置为很明显的铸态组织,并没有任何的过度情况