这种衍射斑点能确定两种相的位向关系吗

A相卡片信息

Orthorhombic,  Cmcm(63)    Z=4    mp=
Cell=6.163x9.728x4.704<90x90x90>    Pearson=
Density(c)=5.08    Density(m)=    Mwt=    Vol=   
Ref= Ibid.

Strong Line: 2.28/X  2.37/7  1.34/5  2.16/4  1.69/4  1.53/3  1.42/3  2.43/2

d(A)    I(f)  I(v)  h  k  l  n^2  2-Theta  Theta  1/(2d)  2pi/d 
3.539  18.0  12.0  1  1  1        25.137  12.568  0.1413  1.7750
2.871    9.0    7.0  1  3  0        31.119  15.560  0.1741  2.1880
2.602  10.0    9.0  2  2  0        34.430  17.215  0.1921  2.4141
2.430  23.0  22.0  0  4  0        36.949  18.475  0.2057  2.5848
2.367  65.0  63.0  0  0  2        37.969  18.985  0.2112  2.6536
2.279  100.0  100.0  2  2  1        39.498  19.749  0.2193  2.7563
2.160  44.0  46.0  0  4  1        41.768  20.884  0.2314  2.9078
2.009    7.0    8.0  3  1  0        45.088  22.544  0.2489  3.1274
1.820    6.0    8.0  1  3  2        50.060  25.030  0.2746  3.4512
1.743  18.0  24.0  2  2  2        52.438  26.219  0.2868  3.6038
1.718    9.0  12.0  1  5  1        53.270  26.635  0.2910  3.6568
1.690  38.0  51.0  0  4  2        54.228  27.114  0.2958  3.7176
1.529  28.0  42.0  3  1  2        60.496  30.248  0.3270  4.1091
1.501    4.0    6.0  1  1  3        61.729  30.864  0.3330  4.1846
1.422  26.0  42.0                65.566  32.783  0.3515  4.4167
1.361  14.0  23.0  1  7  0        68.910  34.455  0.3672  4.6149
1.340  52.0  88.0  2  2  3        70.170  35.085  0.3731  4.6886
1.313    3.0    5.0  0  4  3        71.790  35.895  0.3806  4.7825
1.289  10.0  18.0  4  0  2        73.380  36.690  0.3878  4.8737
1.279  13.0  23.0                74.015  37.008  0.3907  4.9099
1.242    8.0  15.0  4  2  2        76.660  38.330  0.4026  5.0589
1.217  18.0  34.0  0  8  0        78.488  39.244  0.4106  5.1603

B相信息

Cubic,  Pm-3m(221)    Z=.455    mp=
Cell=3.233x3.233x3.233<90x90x90>    Pearson=
Density(c)=4.822    Density(m)=    Mwt=    Vol=   
Ref= Ibid.

Strong Line: 2.29/X  1.62/5  1.32/3  1.02/1  0.86/1

d(A)    I(f)  I(v)  h  k  l  n^2  2-Theta  Theta  1/(2d)  2pi/d 
3.231    1.0    1.0  1  0  0    1  27.585  13.792  0.1548  1.9447
2.287  100.0  100.0  1  1  0    2  39.365  19.683  0.2186  2.7473
1.616  47.0  67.0  2  0  0    4  56.935  28.467  0.3094  3.8881
1.319  34.0  59.0  2  1  1    6  71.463  35.732  0.3791  4.7636
1.143    2.0    4.0  2  2  0    8  84.739  42.370  0.4374  5.4971
1.023  14.0  31.0  3  1  0  10  97.695  48.848  0.4888  6.1419
0.864  12.0  32.0  3  2  1  14  126.132  63.066  0.5787  7.2722