PDF#15-0876: QM=Star(S); d=Diffractometer; I=(Unknown)
Fluorapatite, syn
Ca5 ( P O4 )3 F   
Radiation=CuKa1    Lambda=1.54056    Filter=Ni
Calibration=Internal(W)    2T=10.887-63.298    I/Ic(RIR)=1.50
Ref: d:\应用软件\mdi jade 6.5 portable\pdf\codens.dat missing!

Hexagonal - Powder Diffraction,  P63/m (176)    Z=2    mp=
CELL: 9.3684 x 9.3684 x 6.8841 <90.0 x 90.0 x 120.0>    P.S=hP42 (?)
Density(c)=3.201    Density(m)=3.150    Mwt=504.31    Vol=523.25    F(30)=73.7(.0120,34/0)
Ref: Ibid.

Strong Lines: 2.80/X 2.70/6 2.77/6 3.44/4 2.62/3 1.84/3 1.94/3 2.25/2 3.07/2 1.80/2
NOTE:  Prepared at NBS, Gaithersburg, Maryland, USA, from Ca3 ( P O4 )2.
Spectroscopic analysis: 0.1 to 1.0% each of Mg and Na; and 0.01 to 0.1% each of Al, Ba, Ge, Fe, Si, and Sr.
Pattern taken at 25 C.
To replace 00-003-0736, 00-034-0011 and 00-035-0496.
See ICSD 1709 (PDF 01-070-0796); ICSD 1710 (PDF 01-070-0797); ICSD 9444 (PDF 01-071-0880); ICSD 9445 (PDF 01-071-0881); ICSD 24236 (PDF 01-073-1727); ICSD 27829; ICSD 27830; ICSD 30261 (PDF 01-075-0915); ICSD 34228 (PDF 01-076-0558); ICSD 66573 (PDF 01-079-1572); ICSD 75165 (PDF 01-082-1109); ICSD 79652 (PDF 01-083-0556); ICSD 79653 (PDF 01-083-0557).

2-Theta    d(?)  I(f)  ( h k l)  Theta  1/(2d)  2pi/d  n^2 
10.887  8.1200    8.0  ( 1 0 0)  5.443  0.0616  0.7738   
16.874  5.2500    4.0  ( 1 0 1)  8.437  0.0952  1.1968   
18.930  4.6840    <1  ( 1 1 0)  9.465  0.1067  1.3414   
21.901  4.0550    8.0  ( 2 0 0)  10.950  0.1233  1.5495   
22.949  3.8720    8.0  ( 1 1 1)  11.475  0.1291  1.6227   
25.472  3.4940    <1  ( 2 0 1)  12.736  0.1431  1.7983   
25.863  3.4420  40.0  ( 0 0 2)  12.932  0.1453  1.8254   
28.153  3.1670  14.0  ( 1 0 2)  14.077  0.1579  1.9840   
29.091  3.0670  18.0  ( 2 1 0)  14.546  0.1630  2.0486   
31.936  2.8000  100.0  ( 2 1 1)  15.968  0.1786  2.2440   
32.267  2.7720  55.0  ( 1 1 2)  16.134  0.1804  2.2667   
33.127  2.7020  60.0  ( 3 0 0)  16.563  0.1850  2.3254   
34.141  2.6240  30.0  ( 2 0 2)  17.071  0.1905  2.3945   
35.640  2.5170    6.0  ( 3 0 1)  17.820  0.1986  2.4963   
39.329  2.2890    8.0  ( 2 1 2)  19.665  0.2184  2.7449   
40.040  2.2500  20.0  ( 3 1 0)  20.020  0.2222  2.7925   
40.643  2.2180    4.0  ( 2 2 1)  20.321  0.2254  2.8328   
42.193  2.1400    6.0  ( 3 1 1)  21.097  0.2336  2.9361   
42.443  2.1280    4.0  ( 3 0 2)  21.221  0.2350  2.9526   
43.893  2.0610    6.0  ( 1 1 3)  21.947  0.2426  3.0486   
44.645  2.0280    2.0  ( 4 0 0)  22.323  0.2465  3.0982   
45.377  1.9970    4.0  ( 2 0 3)  22.688  0.2504  3.1463   
46.865  1.9370  25.0  ( 2 2 2)  23.432  0.2581  3.2438   
48.266  1.8840  14.0  ( 3 1 2)  24.133  0.2654  3.3350   
48.873  1.8620    4.0  ( 3 2 0)  24.436  0.2685  3.3744   
49.583  1.8370  30.0  ( 2 1 3)  24.791  0.2722  3.4204   
50.764  1.7970  16.0  ( 3 2 1)  25.382  0.2782  3.4965   
51.563  1.7710  14.0  ( 4 1 0)  25.782  0.2823  3.5478   
52.292  1.7480  14.0  ( 4 0 2)  26.146  0.2860  3.5945   
53.143  1.7220  16.0  ( 0 0 4)  26.572  0.2904  3.6488   
54.440  1.6840    <1  ( 1 0 4)  27.220  0.2969  3.7311   
56.139  1.6370    6.0  ( 3 2 2)  28.070  0.3054  3.8382   
57.283  1.6070    4.0  ( 3 1 3)  28.642  0.3111  3.9099   
58.355  1.5800    2.0  ( 5 0 1)  29.178  0.3165  3.9767   
59.094  1.5620    <1  ( 3 3 0)  29.547  0.3201  4.0225   
60.283  1.5340    6.0  ( 4 2 0)  30.142  0.3259  4.0959   
60.720  1.5240    4.0  ( 3 3 1)  30.360  0.3281  4.1228   
61.751  1.5010    4.0  ( 2 1 4)  30.876  0.3331  4.1860   
61.935  1.4970    4.0  ( 4 2 1)  30.967  0.3340  4.1972   
63.298  1.4680    8.0  ( 5 0 2)  31.649  0.3406  4.2801