各位前辈高手，初次接触透射电镜衍射斑点，缺少经验，望多多指教，学习一下，非常感谢！
以前做练习比较多的是立方结构，六方的比较少，不会计算关于角度的。

Zr的alpha相卡片
d(A)    I(f)  I(v)  h  k  l  n^2  2-Theta  Theta  1/(2d)  2pi/d 
2.798  33.0  29.0  1  0  0        31.959  15.980  0.1787  2.2456
2.573  32.0  31.0  0  0  2        34.840  17.420  0.1943  2.4420
2.459  100.0  100.0  1  0  1        36.510  18.255  0.2033  2.5552
1.894  17.0  22.0  1  0  2        47.995  23.997  0.2640  3.3174
1.616  17.0  26.0  1  1  0        56.935  28.467  0.3094  3.8881
1.463  18.0  30.0  1  0  3        63.540  31.770  0.3418  4.2947
1.399    3.0    5.0  2  0  0        66.815  33.408  0.3574  4.4912
1.368  18.0  32.0  1  1  2        68.537  34.268  0.3655  4.5930
1.350  12.0  22.0  2  0  1        69.581  34.791  0.3704  4.6542
1.287    4.0    8.0  0  0  4        73.526  36.763  0.3885  4.8820
1.229    4.0    8.0  2  0  2        77.577  38.789  0.4066  5.1099
1.168    3.0    6.0  1  0  4        82.444  41.222  0.4278  5.3753
1.084    4.0    9.0  2  0  3        90.545  45.272  0.4612  5.7952
1.058    2.0    5.0  2  1  0        93.355  46.677  0.4722  5.9343
1.036    6.0  14.0  2  1  1        96.063  48.032  0.4826  6.0649
1.006    3.0    7.0  1  1  4        99.895  49.948  0.4969  6.2438